针对港口装卸门机回转齿轮断裂问题，通过材质的焊接性分析，选择出合理有效的焊接工艺方法，降低了焊缝的冷热裂纹敏感性，解决了焊接热影响区的脆化软化问题，提高了焊缝的综合力学性能，获得性能优良的焊接接头，为42CrMo4异种钢焊接的应用和研究奠定理论基础。
Abstract：Regarding to the fracture problem of the rotating gear of the port loading and unloading gantry crane,a reasonable and effective welding process was selected through material welding performance analysis,which reduced the cold and hot crack sensitivity of the weld seam,solved the problem of embrittlement and softening in the welding heat affected zone,improved the comprehensive mechanical properties of the weld seam,and obtained high-performance welding joints,laying a theoretical foundation for the application and research of 42CrMo4 dissimilar steel welding.
[1]冯吉才，王廷，张秉刚，等．异种材料真空电子束焊接研究现状分析[J]．焊接学报，2009,30(10)108-112．
[2]刘东宇，李东，李凯斌，等．E36与304异种金属光纤激光焊接接头的组织分析[J]．激光与光电子学进展，2015,52(4):107-113．
[3]黎丽，唐焱杰，戴伟，等.2205和Q235B异种钢的焊接接头组织及性能分析[J].焊接与切割,2023(12):66-69.
[4]孙恒，王美丽.ASTM A105A与A487 CA6NM异种钢焊接工艺研究[J].技术与市场，2023,30(3)49-52.
[5]李林平，杨茂鸿，杜晋峰，等.Sanicro25/G115异种钢焊接接头的微观组织及力学性能[J].材料热处理学报，2023,44(11)200-208.
[6]金爱龙.SUS304/42CrMo4异种材料激光焊接接头微观组织及力学性能研究[J].机械设计与制造工程，2022,51(12)116-120.
[7]郭十奇，柯美武，陶会丽．42CrMo钢双排链轮轴调质工艺改进[J]．金属热处理，2011,36(6):118-119．
[8]陈俊丹，莫文林，王培，等．回火温度对42CrMo钢冲击韧性的影响[J]．金属学报，2012,48(10):1186-1193．
[9]史可庆．淬火冷却速率对42CrM o4钢风电空心主轴的影响[J]．热处理技术与装备，2019,40(3):34-39．
[10]孙雪盼．42CrMo钢拉杆矫直开裂分析[J]．热处理技术与装备，2019,40(1):64-66．
[11]张金库，张伟强，王大伟，等.42CrMo钢与16Mn钢焊接工艺研究[J].煤矿机械，2010,31(2):102-104.
[12]黄本生，杨江，卢东华，等.Q345/316L异种钢焊接接头显微组织结构与力学性能[J].材料热处理学报，2016,37(5):45-51.
[13]温奇飞，高杨，温飞娟，等.Q345B与20Mn23Al异种钢焊接接头显微组织及力学性能研究[J].焊接技术，2023,52(9):12-16.
[14]周龙，刘同干，郭小钢，等.T92和S30432马氏体/奥氏体异种钢焊接接头硬度研究[J].焊接技术，2023,52(12):25-30.
基本信息:
DOI：10.16825/j.cnki.cn13-1400/tb.2024.05.020
中图分类号:TG457.11;U653.928.3
引用信息:
[1]张磊,毕胜,许秋等.港口装卸门机回转齿轮42CrMo4/Q345钢焊接工艺研究[J].工业技术与职业教育,2024,22(05):6-8.DOI:10.16825/j.cnki.cn13-1400/tb.2024.05.020.
基金信息:
唐山市科技局科学研究项目“大规格BHW35锅炉用钢筒体焊接接头热影响区组织性能研究”(课题编号17110234a)，主持人毕胜